Infiltração marginal de materiais hibridos de ionomero de vidro





























Autor: Alex Jose Souza dos Santos
[pt] Efeito da sinerese “pos-maturação” na infiltração marginal de materiais hibridos de ionomero de vidro/resina composta
Instituição de Defesa: Universidade Estadual de Campinas . Faculdade de Odontologia de Piracicaba
Data de Defesa: 2001-02-13
Resumo: [pt] O objetivo desse estudo in vitro foi avaliar o efeito da sinérese “pós. maturação” na infiltração marginal de materiais restauradores. Cavidades cilíndricas foram preparadas em blocos de esmalte e de dentina, obtidos de superficies coronárias e radiculares de 120 incisivos bovinos. As ~4 – ;F cavidades foram restauradas com Dyract (Dy), Compoglass F (Co), Vitremer (Vi), Fuji II LC (Fu), Ketac-Fil PLus (Ke) e Z 100 (Zl). Os espécimes foram termociclados por 3000 ciclos, entre temperaturas de 5I2°C e 55I2°C, e metade foi submetida à desidratação por 45 minutos em temperatura de 30°C e 60% de umidade relativa do ar. Os espécimes foram imersos em solução aquosa de azul de metileno a 2%, por 12 horas, e a infiltração marginal foi mensurada quantitativamente através de espectrofotometria. A análise estatística ANOV A, seguida pelo teste de Tukey (p <0,05), mostrou diferenças estatísticas significativas entre as médias de infiltração marginal entre os materiais testados no esmalte (Ke[en] The aim of this in vitro study was to evaIuate the effect of the dehydration “post-maturaty” in the microIeakage of gIass-ionomer composite resins hybrids materiaIs. CylindricaI cavities were prepared in scraps of enameI and dentin. These scraps were obtained of the root and coronary surfaces of 120 teeth bovine incisive. The cavities were filling with Dyract (Dy), CompogIass F (Co), Vitremer (Vi), Fuji II LC (Fu) Ketac-FiI PLus (Ke) and Z 100 (Zl). All the sampIes were thermally stressed for 3000 cieles with dwell time at 5:t2°C e 55:t2°C. HaIf of aII the sampIes were submitted to the dehydration by 45 minutes at 30°C and 60% ofreIative humidity ofthe air. The sampIes were immersed in methyIene bIue for 12 hours. The microleakage was quantified spectrophotometrically, and the data were statistically anaIyzed by ANOV A and Tukey test (P <0.05). The resuIts showed significant differences among the microIeakage the materiaIs tested (P <0.01), in the enameI (Ke
Titulação: Mestre em Clinica Odontologica
Contribuidor(es): Luis Thadeu de Abreu Poletto
Jose Roberto Lovadino [Orientador]
Jose Roberto Lovadino
Luis Alexandre M. S. Paulillo
Assuntos: [pt] Materiais dentarios
[pt] Dentistica